XOANONS®Dispersant
It is used for the dispersion and viscosity reduction of nano-slurries such as silicon carbide, silicon nitride, boron carbide, boron nitride and conductive carbon black in aqueous systems.

Product Code
XOANONS®LD 1217-45W

Physicochemical Index

Item	Specification	Test Method/Equipment	Test Standard
Composition	Styrene-maleic acid copolymer solution	---	---
Appearance	Slightly yellow to yellow slightly turbid liquid	---	---
Content	45±3 %	Electric hot blast drying oven (125℃×1h)	GB/T 1725-2007
Density	1.06-1.10 g/ml	Pycnometer	GB/T 6750-2007
Viscosity	10-50s	Ford Cup #4	GB/T 1723-1993
pH	4-7	Glass electrode method	GB/T 9724-2007

Note: These indexes represent typical results only and are not regarded as specifications. The actual Certificate of Analysis (COA) shall prevail.

Application Field
Dispersion, viscosity reduction and solid content improvement in the grinding of nano-grade inorganic powder materials such as silicon carbide, silicon nitride, boron carbide and boron nitride, as well as in the ceramic slurry preparation section in aqueous systems.

Key Feature
Provides steric hindrance to increase the solid content of slurries;
Reduces undesirable phenomena such as sedimentation and flocculation of slurries;
Improves the storage stability of slurries.

Usage Method
First, add XOANONS®LD 1217-45W dispersant into deionized water and stir evenly, then add powder materials according to the formula ratio for dispersion and grinding together.

Recommended Dosage
Addition amount (as purchased) is 5-10% based on the weight of powder materials.

Storage Stability
Seal and store in a dark place. The shelf life is 24 months in the unopened original packaging. Products beyond the shelf life can be used continuously after passing inspection. Tightly seal the container immediately after use if it is not completely empty.

Package
25 kg (plastic barrel)