XOANONS® Dispersant
Used for lipophilic alumina coating treatment and dispersion viscosity reduction of separator slurry

Product Code
XOANONS®LD 1235

Physicochemical Index

Item	Specification	Test Method/Equipment	Test Standard
Composite	Modified polyethylene glycol	---	---
Appearance	Yellow transparent liquid	---	---
Solid content	50%	Electric hot blast drying oven （120℃×1h）	GB/T 1725-2007
Solvent	Water	---	---
Density	1.09-1.13g/mL	Pycnometer	GB/T 6750-2007
Viscosity	500-1500 mPa·s	Digital rotary viscometer	GB/T 15357-2014
pH value	2.0-5.0	Glass electrode method	GB/T 9724-2007

Note: This data sheet is intended to give typical results, not standard. Subject to COA.

Application Field
Iron oxide red method LFP precursor slurry

Property
When applied to the red iron oxide-based LFP precursor slurry, it serves as a substitute for PEG, delivering superior wetting and dispersion performance, effectively increasing the solid content of the slurry while reducing costs and improving efficiency.
Effectively improve compaction density and electrical conductivity.

Usage Method
Add the dispersant XOANONS® LD 1235 to water, stir thoroughly to dissolve, and then add it to the slurry according to the specified dosage and grind/dispers together.

Recommended Dosage
Addition amount (in purchased form): Based on powder, 2–10%.

Storage Stability
Keep intact 24 months in original package. Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Package
25KG/180KG (plastic drum)