XOANONS® Leveling agent for anti-pinhole
Used for the preparation of water-based diaphragm coating and carbon-coated aluminum foil paste, which can significantly reduce the surface tension, improve the substrate wetting and leveling properties, and increase the adhesion to the substrate

Product Code
XOANONS®LD 1710

Physicochemical Index

Item	Specification	Test Method/Equipment	Test Standard
Composite	Polyether modified  polysiloxane copolymer	---	---
Appearance	Colorless to slightly yellowish transparent liquid	---	---
Active content	50%	---	---
Solvent	——	---	---
Density	0.98-1.02 g/ml	Pycnometer	GB/T 6750-2007
Viscosity	7-24s	Tu-4 cup	GB/T 1723-1993

Note: This data sheet is intended to give typical results, not standard. Subject to COA.

Application Field
Water-based

Property
It can strongly reduce the surface tension of water system, have excellent wetting and spreading ability, and prevent the generation of shrinkage hole.
Good anti-foaming property.
Increase the adhesion to the substrate.
Help level the slurry on porous polyolefin separators and enables fast, defect-free coating of anode slurry on copper foil.

Usage Method
Pre-dilute in water according to the form of supply, stir evenly and add to the slurry.

Recommended Dosage
Addition amount (total formulation) 0.05-1.5%

Storage Stability
Keep intact 24 months in original package. Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Package
25KG/180KG (plastic drum)