XOANONS® Dispersing agent
Used for preparing carbon nanotube slurry

Product Code
XOANONS®LD1132C-50

Physicochemical Index

Item	Specification	Test Method/Equipment	Test Standard
Composite	Modified styrene maleic anhydride copolymer solution	---	---
Appearance	Yellow to reddish brown transparent liquid	---	---
Content	50%	Electric hot blast drying oven （110℃×1h）	GB/T 1725-2007
Solvent	1-Methyl-2-pyrrolidone	---	---
Density	1.08-1.12 g/ml	Pycnometer	GB/T 6750-2007
Viscosity	50-500 mPa·s	Digital rotary viscometer	GB/T 15357-2014
pH value	9-13	Glass electrode method	GB/T 9724-2007
Refractive index	1.478-1.482	Abbe refractometer	GB/T 6488-2008

Note: This data sheet is intended to give typical results, not standard. Subject to COA.

Application Field
Multi-walled cobalt-based array tubes and iron-based winding tubes in solvent-based

Property
Provide steric hindrance, adding it to the slurry can significantly reduce the viscosity of the conductive slurry; Improve the fluidity of the slurry;
Reduce adverse phenomena such as sedimentation and flocculation of the slurry; The storage stability of the slurry is excellent.

Usage Method
Add the dispersant XOANONS®LD1132C-50 to the solvent, stir evenly. Then add it to the slurry according to the formula and grind and disperse it together.

Recommended Dosage
Addition amount (purchase form) for carbon nanotubes or graphene: 20-100%.

Storage Stability
Keep intact 24 months in original package. Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Package
25KG (plastic drum)