XOANONS® Dispersing agent
Used for preparing conductive carbon nanotube slurry

Product Code
XOANONS®LD 1126

Physicochemical Index

Item	Specification	Test Method/Equipment	Test Standard
Composite	Block co-polymers with conjugated groups	---	---
Appearance	Yellow viscous liquid to the paste (viscous in summer and paste in winter)	---	---
Content	60±3%	Electric hot blast drying oven （125℃×1h）	GB/T 1725-2007
Solvent	1-Methyl-2-pyrrolidone	---	---
Density	1.02-1.06g/ml	Pycnometer	GB/T 6750-2007
Viscosity	5-25s	LD-1126：NMP=10：90，Tu-4	GB/T 1723-1993
pH value	7-10	LD-1126：NMP=10：90， Glass Electrode method	GB/T 9724-2007
Moisture	＜1.5%	Automatic moisture titrator	GB/T 6283-2008
Refractive index	1.466-1.470	Abbe refractometer	GB/T 6488-2008

Note: This data sheet is intended to give typical results, not standard. Subject to COA.

Application Field
Multi-walled cobalt-based array tubes and iron-based winding tubes in solvent-based

Property
Provide steric hindrance, which can significantly reduce the viscosity of the conductive carbon black slurry; improve the fluidity of the slurry;
Reduce adverse phenomena such as sedimentation and flocculation of the slurry; The storage stability of the slurry is excellent.

Usage Method
Add to NMP, stir and dissolve at 10% solid content, then add conductive carbon black and mix for grinding.

Recommended Dosage
Addition amount (purchase form) for carbon black: 20-100%.
The above suggested addition levels have little effect on resistance; the optimal addition amount needs to be determined through a series of tests.

Storage Stability
Keep intact 24 months in original package. Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Package
25KG ((plastic drum lined with aluminum-plastic bag))