XOANONS® Polyester modified silicon leveling agent

Model number
XOANONS®WE-D510

Specification
Composition: Polyester modified polydimethyl siloxane solution
Appearance: Transparent to slight yellowish clear liquid(paste at low temperature)
Solvent : PMA
Density : 0.95-0.99g/ml(25±1)℃
Viscosity : 5-25s(Tu-4 viscometer)(25±0.2)℃
Content: 25±3%(105℃ 3h)
Note: This data sheet is intended to give typical results, not standard.
Subject to COA.

Application system
Solvent-based, UV Cure

Properties
Reduce the friction coefficient. Increase slip and improve scratch resistance.
Suit for high temperature baking finish system, good recoating and do not influence adhesion of coating films.
Combination with WE-D9013R will prevent cratering and reduce dynamic surface tension.(Increase spray leveling speed, and anti-orange-peel ability.
It precipitates at low temperatures. It would become clear and flow after heated or diluted with solvent. This will not influence the quality.

Incorporation
Can add in any stage during the production process including post-addition.

Suggest addition
Addition to total formulation 0.1-0.5%

Storage stability
Keep intact 24 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Application recommendation

Transparency in varnish	4
Defoaming	2
Dynamic surface tension	3
Static surface tension	3
Slip	4
Prevent orange peel	2

0=unavailable 5=very effective

Package
25KG / 180KG