JIAZHI® easy-cleaning functional resin

Model number
JIAZHI®JZ-9545

Specification
Composition: Silicone modified hydroxyl acrylic resin solution
Appearance : Slight yellowish to yellow liquid
Solvent : PMA
Content: 50±3%(140℃ 2h)
Density : 1.02-1.06g/ml(25±1)℃
Viscosity: 6000-16000mPa·s (Rotating viscometer)(25±0.2)℃
Hydroxyl value: 152±5 mg KOH/g (Theoretical value of solid resin)
Note: This datasheet is intended to give typical results, not standard. Subject to COA.

Application system
Solvent-based system

Properties
● Increase slip. Improve hydrophobicity and oleophobicity.
● Provide anti-marker wiping performance.
● Provide lotus effect.
● Compared with anti-graffiti additive, better easy cleaning effect and alcohol-resistant wiping performance.
● Water contact angle＞100°
● Excellent anti-graffiti effect in light paint.
● Low temperature curing also has good easy cleaning effect.

Storage stability
Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.

Recommended formula
1. Suggestion for PU varnish formulation

	Material	Dosage%
Part A	JZ-9545	60
	PMA	39.15
	Dryer(1%)	0.3
	WE-D8920CR(leveling agent)	0.25
	WE-D912R(defoamer)	0.3
	Total	100
Part B	N3390	18

1.NCO% of N3390=19.6, produced by Covestro, Germany.
2. After mixing A and B components, the storage period is 5-7 hours under the condition of a lid. Therefore, mixed materials should be used as soon as possible, otherwise it will be gelatinized and cannot be used.
3.Recommended baking temperature: 80 ° C for 1 hour or 150 ° C for 5 minutes, which could have better easy cleaning effect.

2. Suggestion for baking system formulation

Material	Dosage
JZ-9545	50
Butylated amino resin	10
Solvent	38.5
Adhesion promoter	1
Acid catalyst	0.5
Total	100

Recommended baking temperature: 150 ° C for 30 minutes or 210 ° C for 90 seconds.

Package
25KG / 180KG