JIAZHI® easy-cleaning functional resin

Model number
JIAZHI®JZ-9510B

Specification
Composition: Silicone modified hydroxy acrylic resin solution
Appearance : Slight yellowish to yellow liquid
Solvent : PGMEA/BAC
Content: 50±3%(140℃ 2h)
Density : 0.99-1.03g/ml(25±1)℃
Viscosity : 1000-6000mPa·s (Rotating viscometer)(25±0.2)℃
Hydroxyl value: 120±5 mg KOH/g (Theoretical value of solid resin)
Note: This datasheet is intended to give typical results, not standard. Subject to COA.

Application system
Solvent-based system

Properties
● Increase slip. Improve hydrophobicity and oleophobicity.
● Provide anti-marker wiping performance.
● Provide lotus effect.
● Excellent varnish compatibility.
● Compared with anti-graffiti additive, better easy cleaning effect and alcohol-resistant wiping performance.
● Water contact angle＞100°

Storage stability
Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.

Recommended formula
1. Suggestion for PU varnish formulation

	Material	Dosage%
Part A	JZ-9510B	76
	PMA	22.45
	Dryer(1%)	1
	WE-D8920CR(leveling agent)	0.25
	WE-D912R(defoamer)	0.3
	Total	100
Part B	N3390	18

1.NCO% of N3390=19.6, produced by Covestro, Germany.
2. After mixing A and B components, the storage period is 5-7 hours under the condition of a lid. Therefore, mixed materials should be used as soon as possible, otherwise it will be gelatinized and cannot be used.
3. Recommended baking temperature: 80 ° C for 1 hour or 150 ° C for 5 minutes, which could have better easy cleaning effect.

2. Suggestion for baking system formulation

Material	Dosage
JZ-9510B	50
Amino resin	10
Solvent	38.5
Adhesion promoter	1
Acid catalyst	0.5
Total	100

Recommended baking temperature: 150 ° C for 30 minutes or 210 ° C for 90 seconds.

Package
25KG / 180KG