XOANONS^® dispersant

 

It is used for the dispersion, viscosity reduction, and improvement of compaction density and electrical conductivity of LFP precursor slurry prepared by the iron oxide red method

Product Number                       

XOANONS ® LD 1235

        

Physical and chemical indexes

Item	Indexes	Test method or device	Testing standards
Composition	Modified polyethylene glycol	---	---
Appearance	Orange-yellow slightly turbid - transparent liquid	---	---
Solid content	50%	Electric blast drying oven (120°C×1h)	GB/T 1725-2007
Solvents	Water	---	---
Density	1.09-1.13g/mL	Specific Gravity cup	GB/T 6750-2007
Viscosity	500-1500 mPa·s	Rotary viscometer	GB/T 15357-2014
pH	2.0-5.0	Glass electrode method	GB/T 9725-2007

Note: These Indexes represent typical results only and are not considered specifications, based on specific COAs.

 

Applications :

Iron oxide red method LFP precursor slurry

Key features

It can replace PEG and have a better wetting and dispersion effect, which can effectively improve the solid content of the slurry, reduce costs and increase efficiency.
Effectively improve compaction density and conductivity.

 

How to use

dispersant XOANONS ® LD 1235 is added to water, stirred to dissolve, and then added to the slurry according to the recipe amount and ground and dispersed together.

 

 

Suggested dosage

Addition ( purchase form ) Based on powder 2-10%.

 

Storage stability

Seal and store in a dark place. Store for 24 months in its original unopened packaging. Products that have exceeded the storage period can continue to be used after passing the inspection. The container is not completely used and must be closed immediately after use.

 

 

Packaging

25 kg (plastic drum) / 180 kg (plastic drum).