XOANONS^® Polyether modified silicon leveling agent

Model number
XOANONS^®WE-D5527

Specification
Composition: Double-end hydroxyl polyether modified polysiloxane copolymer
Appearance: slight yellowish to yellow clear liquid(paste at low temperature)
Solvent: ----
Density: 1.01-1.05g/ml(25±1)℃
Viscosity: F-M(Bubble viscometer)(25±0.2)℃
Active content: 100%
Flash point: ＞100℃
Note: This data sheet is intended to give typical results, not standard.Subject to COA.

Application system
Solvent-based coating, PU synthetic leather

Properties
Replace part polyether polyols to copolymerization with isocyanate when synthetic sizing agent. Improve softness, lubricating property and ydrophobicity of organic resin from structure. Improve hydrolytic stability of PUR. The coating effect is lasting. No migration problem of blending modification silicone.
Higher solubility than normal silicon, not only can dissolve in water, alcohol system, but also can be used for oil system, even 10% addition.
Improve smooth performance when add to synthetic fiber processing.

Incorporation
Add directly or dilute the stock solution with organic solvent or water before adding it to the resin system, and pre-dilute it to 20% before adding it to the aqueous system.

Suggest addition
Addition to total formulation 0.05-0.5%
Resin modification (for amount of resin) 1-5%

Storage stability
Keep intact 24 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.

Package
25KG / 180KG