JIAZHI^® easy-cleaning functional resin

Model number
JIAZHI^®JZ-9515

Specification
Composition: Silicone modified hydroxy acrylic resin solution
Appearance: Transparent clear liquid
Solvent: BAC
Content: 50±3%(140℃ 2h)
Density: 0.98-1.02g/ml(25±1)℃
Viscosity: 15000-35000mPa·s(Rotating viscometer)(25±0.2)℃
Hydroxyl value 152±5 mg KOH/g(Theoretical value of solid resin)
Note: This datasheet is intended to give typical results, not standard. Subject to COA.

Application system
Solvent-based system

Properties
● Increase slip. Improve hydrophobicity and oleophobicity.
● Provide anti-marker wiping performance.
● Provide lotus effect.
● Compared with anti-graffiti additives, it has better anti-painting effect and solvent resistance wiping performance.
● Water contact angle > 100°.
● Excellent anti-graffiti effect in light-colored paints.
● Low-temperature curing has a good anti-graffiti effect.

Storage stability
Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.

Recommended formula
1. Suggestion for PU varnish formulation

1.NCO% of N3390=19.6, produced by Covestro, Germany.
2. After mixing A and B components, the storage period is 5-7 hours under the condition of a lid. Therefore, mixed materials should be used as soon as possible, otherwise it will be gelatinized and cannot be used.
3. Recommended baking temperature: 80 ° C for 1 hour or 150 ° C for 5 minutes, which could have better easy cleaning effect.

2. Suggestion for baking system formulation

Recommended baking temperature: 150 ° C for 30 minutes or 210 ° C for 90 seconds.

Package
25KG / 180KG