Anhui Xoanons Chemical Co.,Ltd.

Anhui Xoanons Chemical Co., Ltd.

PRODUCTS

XOANONS®Additive

Surfactant
Polyacrylate leveling agent
Fluorocarbon modified polyacrylate leveling agent
Fluorine surfactant
Polyether modified silicon leveling agent
Reactive silicon additive with acrylic functional group
Substrate wetting agent
Anti-graffiti additive
Performance enhancer
Dispersant
Defoamer

JIAZHI® Easy-cleaning functional resin

Anti-graffiti and Anti-adhesive Resin for municipal engineering paint
Anti-pollution and rain-resistant resin for protective film of paint
Easy-cleaning resin for industrial paint
Anti-icing resin
Anti-graffiti resin for automotive leather and sofa leather
Anhui Xoanons Chemical Co.,Ltd.

PRODUCTS

JIAZHI® JZ-9522

Model number

JIAZHI®JZ-9522

Specification

Composition     

Silicone modified hydroxyl acrylic resin solution

Appearance      

Slight yellowish to yellow clear liquid

Solvent            

BAC/PMA

Content

50±3%(140℃ 2h)

Density         

1.00 -1.04g/ml(25±1)℃

Viscosity        

1000 -6000mPa·s
(Rotating viscometer)(25±0.2)℃

Hydroxyl value

152±5 mg KOH/g
(Theoretical value of solid resin)

 

Note: This datasheet is intended to give typical results, not standard. Subject to COA.

 

Application system

Solvent-based system

Properties

● Increase slip. Improve hydrophobicity and oleophobicity.

● Provide anti-marker wiping performance.

● Provide lotus effect.

● Compared with anti-graffiti additive, better anti-graffiti effect and solvent-resistant wiping performance.

● Water contact angle>100°

● Excellent anti-graffiti effect in light paint.

● Low temperature curing also has good anti-graffiti effect.

Storage stability

Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.

Recommended formula
1. Suggestion for PU varnish formulation 

 

Material

Dosage%

Part A

JZ-9522

76

 

PMA

22.65-22.74

 

Dryer(1%)

1

 

WE-D8920BR(leveling agent)

0.25

 

WE-D980(defoamer)

0.01-0.1

 

Total

100

Part B

N3390

23

1. Suggestions for the use of defoamers
Adding 0.01% XOANONS®WE-D980 to PU varnish does not affect the transparency of the paint solution; The color paint system can increase the amount of XOANONS®WE-D980 added by 0.1%.
2.NCO% of N3390=19.6, produced by Covestro, Germany.
3. After mixing A and B components, the storage period is 5-7 hours under the condition of a lid. Therefore, mixed materials should be used as soon as possible, otherwise it will be gelatinized and cannot be used.
4. Recommended baking temperature: 80 ° C for 1 hour or 150 ° C for 5 minutes, which could have better easy cleaning effect.
2. Suggestion for baking system formulation

Material

Dosage

JZ-9522

50

Butylated amino resin

10

Solvent

38.5

Adhesion promoter

1

Acid catalyst

0.5

Total

100

1.The amino resin used in this formulation is SANMU 582, which can be further adjusted according to specific requirements.

2. Recommended baking temperature: 150 ° C for 30 minutes or 210 ° C for 90 seconds.