Model number
JIAZHI®JZ-9546
Specification
Composition |
Fluorosilicon modified hydroxyl acrylic resin solution |
|
Appearance |
Slight yellowish to yellowish liquid |
|
Solvent |
BAC/ PMA/ Xylene |
|
Content |
50±3%(105℃ 2h) |
|
Density |
1.05-1.09g/ml(25±1)℃ |
|
Viscosity |
100-1000mPa·s |
|
Hydroxyl value |
76±5 mg KOH/g |
|
Note: This datasheet is intended to give typical results, not standard.Subject to COA.
Application system
Solvent-based
Properties
Increase slip. Improve hydrophobicity and oleophobicity.
Provide anti-marker wiping performance.
Provide lotus.
Excellent flexibility.
Excellent scratch and wear resistance.
Compared with anti-graffiti additive, better anti-graffiti effect and sovlent-resistant wiping performance.
Excellent weather resistance.
Recommended formula
1. Suggestion for PU varnish formulation
|
Material |
Dosage% |
Part A |
JZ-9546 |
76.0 |
PMA |
22.65-22.74 |
|
Dryer(1%) |
1.0 |
|
WE-D8920BR(leveling agent) |
0.25 |
|
WE-D980(defoamer) |
0.01-0.1 |
|
Total |
100 |
|
Part B |
N3390 |
11.5 |
Note：
1.Usage recommendation for defoamer Add WE-D980 with 0.01% to PU varnish and no affecting of compatibility.
Can increase the addition to 0.1% of WE-D980 to color paint.
2.NCO% of N3390=19.6, produced by Covestro, Germany.
3.The mixed part A and B should be used up within 5-7 hours in a sealed container. Otherwise, the mixed material will be gelled.
4.Suggest dry it at 80℃ for 1h or 150℃ for 5min.
Storage stability
Keep intact 36 months in original package.Products beyond the storage period may continue to be used after inspection. The container must be closed immediately after use.
package
25KG / 180KG